Análisis del desempeño biomecánico y químico de diferentes materiales bioactivos en restauraciones clase II
Gorde:
| Egilea: | |
|---|---|
| Formatua: | tesis de maestría |
| Argitaratze data: | 2022 |
| Deskribapena: | Abstract The aim of this in vitro study was to evaluate the biomechanical and chemical behavior of various bioactive materials in class II MOD restorations. Forty-eight standardized class II MOD cavities were prepared in sound extracted human molar teeth. The specimens were divided into four groups according to the restorative material: Group 1 (Filtek™ Z350 XT), Group 2 (Biodentine™ as a liner, and then restored with Filtek™ Z350 XT), Group 3 (Cention N™), and Group 4 (Activa™ Bioactive-Restorative). The samples were tested for fracture resistance by subjecting them to a compressive load in a Universal testing Machine. The failure modes of each specimen were evaluated. The alkalinizing potential and calcium ion release of the materials were measured. SEM-EDAX analyses were also performed for all materials. Data were analyzed using ANOVA and post hoc Tukey test (p<0.05). Group 1 showed the higher fracture resistance (p<0.05). Group 3 had greater fracture resistance values but no statistical difference from Group 4. Biodentine™ showed greater biomineralization potential. Class II MOD restorations of group 1 displayed the higher fracture resistance; however, it was highly associated with catastrophic failure. Conversely, Biodentine™ presented a more significant bioactivity potential, and its use, as in group 2, promoted the most favorable failure mode. |
| Herria: | Kérwá |
| Erakundea: | Universidad de Costa Rica |
| Repositorio: | Kérwá |
| Hizkuntza: | Español |
| OAI Identifier: | oai:kerwa.ucr.ac.cr:10669/87053 |
| Sarrera elektronikoa: | https://hdl.handle.net/10669/87053 |
| Gako-hitza: | Bioactive materials Class II restorations Composite resins Fracture resistance |