Structural Characterization of Chitosan Modified Vesicles
Đã lưu trong:
| Nhiều tác giả: | , , , , , , |
|---|---|
| Định dạng: | artículo original |
| Trạng thái: | Versión publicada |
| Ngày xuất bản: | 2018 |
| Miêu tả: | L-α-phosphatidylcholine (PC) and PC/phosphoglycerol based-vesicles were characterized by means of Dynamic Light Scattering (DLS), Cryo-Scanning Electron Microscopy (Cryo-SEM), and Isotermal Titration calorimetry (ITC). The incorporation of phosphoglycerol into the PC vesicles decreased the size and the polydispersity of the particles, due to an increase of the packing of the aliphatic chains in the palisade layer. This phenomenon has been interpreted in terms of strong van der Waal interactions. The addition of phosphoglycerols resulted in a reduction in zeta potential (ξ) to values of -75 mV, compared to PC based-vesicles. Both systems were modified by using a high molecular weight chitosan (865 kDa) with a degree of deacetylation of 77%. Strong electrostatic interactions between the cationic polyelectrolyte and the vesicles were determined by ITC experiments. The results were reinforced by means of Z potential analysis. It has been demonstrated that a complete inverse of the vesicle surface charge is not required to perform a complete coating of the phospholipid particles. The addition of concentration of chitosan above 0,1 mg/mL induced vesicles aggregation. Aggregated vesicle-polymer structures were visualized by Cryo-SEM and measured by DLS. This behavior was more significant for the PC/DMPG-Na-/chitosan system. |
| Quốc gia: | Portal de Revistas UNA |
| Tổ chức giáo dục: | Universidad Nacional de Costa Rica |
| Repositorio: | Portal de Revistas UNA |
| Ngôn ngữ: | Español |
| OAI Identifier: | oai:ojs.www.una.ac.cr:article/10170 |
| Truy cập trực tuyến: | https://www.revistas.una.ac.cr/index.php/uniciencia/article/view/10170 |
| Từ khóa: | vesicles chitosomes phospholipids polyelectrolytes surface modification. Vesículas quitosomas fosfolípidos polielectrolitos modificación de superficies. |