Una tecnica para obtener la fase icosahedrica en peliculas delgadas multicapas de AICr
Đã lưu trong:
| Nhiều tác giả: | , , , |
|---|---|
| Định dạng: | artículo original |
| Trạng thái: | Versión publicada |
| Ngày xuất bản: | 1993 |
| Miêu tả: | A method used to produce thin films multilayers of AlCr in vacuum system by electron-beam is discribed. The samples with icosahedral phase undergoes in situ annealing when layers of evaporated material condense on hot substrates (approximately 360°C). Diffraction patterns from Transmission Electron Microscopy were used to identify the icosahedral phase. Samples with phase are compared with others grown on substrates at 100°C. |
| Quốc gia: | Portal de Revistas UNA |
| Tổ chức giáo dục: | Universidad Nacional de Costa Rica |
| Repositorio: | Portal de Revistas UNA |
| Ngôn ngữ: | Español |
| OAI Identifier: | oai:ojs.www.una.ac.cr:article/5462 |
| Truy cập trực tuyến: | https://www.revistas.una.ac.cr/index.php/uniciencia/article/view/5462 |
| Từ khóa: | tecnica icosahedrica peliculas multicapas |